Title: Development of a high strength Al-Mg2Si-Mg-Zn based alloy for high pressure die casting
Authors: Ji, S
Yan, F
Fan, Z
Keywords: Aluminium alloys;High pressure die casting;Mechanical property;Microstructure
Issue Date: 2015
Publisher: Elsevier Ltd
Citation: Materials Science and Engineering A, 626: 165 - 174, (February 2015)
Abstract: A high strength Al-Mg2Si-Mg-Zn based alloy has been developed for the application in high pressure die casting to provide improved mechanical properties. The effect of various alloying elements on the microstructure and mechanical properties including yield strength, ultimate tensile strength and elongation of the alloy was investigated under the as-cast and heat-treated conditions. The typical composition of the high strength alloy has been optimised to be Al-8.0wt%Mg2Si-6.0wt%Mg-3.5wt%Zn-0.6wt%Mn (Al-11.0wt%Mg-2.9wt%Si-3.5wt%Zn-0.6wt%Mn) with unavoidable trace impurities. The mechanical properties of the alloy were enhanced by a quick solution treatment followed by ageing treatment. The improved tensile properties were at a level of yield strength over 300MPa, the ultimate tensile strength over 420MPa and the elongation over 3% assessed using international standard tensile samples made by high pressure die casting. The microstructure of the die-cast alloy consisted of the primary α-Al phase, Al-Mg2Si eutectics, AlMgZn intermetallics and α-AlFeMnSi intermetallics under the as-cast condition. The AlMgZn intermetallic compound was dissolved into the Al-matrix during solution treatment and subsequently precipitated during ageing treatment for providing the effective improvement of the mechanical properties.
URI: http://www.sciencedirect.com/science/article/pii/S0921509314015068
http://bura.brunel.ac.uk/handle/2438/11016
DOI: http://dx.doi.org/10.1016/j.msea.2014.12.019
ISSN: 0921-5093
Appears in Collections:Brunel Centre for Advanced Solidification Technology (BCAST)

Files in This Item:
File Description SizeFormat 
Fulltext.pdf2.18 MBAdobe PDFView/Open


Items in BURA are protected by copyright, with all rights reserved, unless otherwise indicated.